| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 0.04 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.39-1.43 | ||
| 玻璃纖維含量 | Ash | 15 | % | ||
| 成型收縮率 | ASTM D-955 | 0.2-1.4 | % | ||
| 機械性能 | IZOD沖擊強度 | ASTM D-256 | 5-7 | Kg.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 93 | M-Scale | ||
| 引張伸長率 | ASTM D-638 | 4-5 | % | ||
| 撓曲強度 | ASTM D-790 | 1300-1500 | Kg/cm2 | ||
| 撓曲彈性率 | ASTM D-790 | 40000-50000 | Kg/cm2 | ||
| 引張強度 | ASTM D-638 | 800-1000 | Kg/cm2 | ||
| 電氣性能 | 表面電阻率 | ASTM D-257 | >1014 | Ω | |
| 誘電正接 | 60Hz | ASTM D-150 | 0.001 | ||
| 絕緣破壞強度 | ASTM D-149 | 20 | KV/mm | ||
| 體積電阻率 | ASTM D-257 | >1016 | Ω.cm | ||
| 誘電率 | 60Hz | ASTM D-150 | 3.3 | ||
| 耐電弧性 | ASTM D-495 | 129 | sec | ||
| 熱性能 | 熱變形溫度 | 4.6Kg/cm2 | ASTM D-648 | 220 | ℃ |
| 線膨脹系數(shù) | ASTM D-696 | 5 | 10-5cm/cm℃ | ||
| 熔點 | DSC | 225 | ℃ | ||
| 熱變形溫度 | 18.6Kg/cm2 | ASTM D-648 | 206 | ℃ | |
| 耐燃性 | 0.83mm | UL 94 | HB | ||
PBT性質(zhì)：為高結晶性熱可塑性塑料，熔點220~230℃，結晶速率比PET快。
PBT優(yōu)點：機械性質(zhì)安定抗張強度與抗張模數(shù)和尼龍相似、摩擦系數(shù)小有自潤性、吸水率低、電氣性質(zhì)優(yōu)良、尺寸安定性良好、耐藥品性、耐油性極佳。缺 點：Tg(30℃)低，在荷重下H.D.T.為60℃、抗沖擊強度不良，一般以玻纖補強為FR-PBT來使用.
PBT用 途：1)、電子電器：無熔線斷電器、電磁開關、馳返變壓器、家電把手、連接器、外殼. 2)、汽車： 車門把手、保險桿、分電盤蓋、擋泥板、導線護殼、輪圈蓋工業(yè)零件：OA風扇、鍵盤、釣具卷線器、零件、燈罩.
PBT 基礎創(chuàng)新塑料(美國) SABIC Valox PBT(聚對苯二甲酸丁二醇脂)：
Valox DR51M特性：15％玻璃纖維增強型PBT.機械/熱/電氣性能強; 阻燃.用于聚光燈,家電外殼和處理.易流動,易脫模.
PBT理化特性 : PBT為乳白色半透明到不透明、結晶型熱塑性聚酯。具有高耐熱性、韌性、耐疲勞性，自潤滑、低摩擦系數(shù)，耐候性、吸水率低，僅為0.1%，在潮濕環(huán)境中仍保持各種物性（包括電性能），電絕緣性，但體積電阻、介電損耗大。耐熱水、堿類、酸類、油類、但易受鹵化烴侵蝕，耐水解性差，低溫下可迅速結晶，成型性良好。缺點是缺口沖擊強度低 ，成型收縮率大 。故大部分采用玻璃纖維增強或無機填充改性，其拉伸強度、彎曲強度可提高一倍以上，熱變形溫度也大幅提高。可以在140℃下長期工作，玻纖增強后制品縱、橫向收縮率不一致，易使制品發(fā)生翹曲。